Most ceramics show an increase of the crack growth resistance during crack propagation (R-curve behaviour). Reasons for such behaviour are bridging effects between opposite crack surfaces, phase transformations around the tip of a crack, and development of micro-cracking zones. This booklet predominantly deals with the bridging behaviour and the discussion of the observed effects in terms of the fracture mechanics weight function procedure.